Cubic Space Groups from 195-230

The following table lists all 36 possible crystallographic cubic space groups (from 195 to 230), their respective symmetry and in brackets to which of the 17 possible aspects they belong.


195. P 2 3 (1) 196. F 2 3 (13) 197. I 2 3 (8) 198. P 21 3 (2)
199. I 21 3 (8) 200. P m -3 (1) 201. P n -3 (4) 202. F m -3 (13)
203. F d -3 (15) 204. I m -3 (8) 205. P a -3 (7) 206. I a -3 (10)
207. P 4 3 2 (1) 208. P 42 3 2 (2) 209. F 4 3 2 (13) 210. F 41 3 2 (14)
211. I 4 3 2 (8) 212. P 43 3 2 (3) 213. P 41 3 2 (3) 214. I 41 3 2 (9)
215. P -4 3 m (1) 216. F -4 3 m (13) 217. I -4 3 m (8) 218. P -4 3 n (5)
219. F -4 3 c (16) 220. I -4 3 d (11) 221. P m -3 m (1) 222. P n -3 n (6)
223. P m -3 n (5) 224. P n -3 m (4) 225. F m -3 m (13) 226. F m -3 c (16)
227. F d -3 m (15) 228. F d -3 c (17) 229. I m -3 m (8) 230. I a -3 d (12)
       


Reference: J.S.Kasper and K.Lonsdale, Eds (1967), in: International Tables for X-Ray Crystallography, Vol 2, page 147 (Table 3.8.6B)


Author: Manfred Kriechbaum Manfred.Kriechbaum@tugraz.at (Nov.18th 2002)